ʻO ka hoʻopaʻa ʻana o nā metala refractory

1. Kūʻai

Hiki ke hoʻohana ʻia nā ʻano mea kūʻai a pau me ka mahana haʻahaʻa ma mua o 3000 ℃ no W brazing, a hiki ke hoʻohana ʻia nā mea kūʻai keleawe a i ʻole kālā no nā ʻāpana me ka mahana ma lalo o 400 ℃;Hoʻohana mau ʻia nā metala hoʻopiha gula, ka manganese, ka manganese, ka palladium a i ʻole ka drill no nā mea i hoʻohana ʻia ma waena o 400 ℃ a me 900 ℃;No nā ʻāpana i hoʻohana ʻia ma luna o 1000 ℃, hoʻohana nui ʻia nā metala maʻemaʻe e like me Nb, Ta, Ni, Pt, PD a me Mo.ʻO ka mahana hana o nā mea i hoʻopaʻa ʻia me ka platinum base solder ua hiki i 2150 ℃.Inā hoʻokō ʻia ka lāʻau diffusion 1080 ℃ ma hope o ka brazing, hiki ke piʻi ka mahana hana kiʻekiʻe i 3038 ℃.

ʻO ka hapa nui o nā mea kūʻai aku i hoʻohana ʻia no ka brazing w hiki ke hoʻohana ʻia no ka brazing Mo, a hiki ke hoʻohana ʻia nā mea kūʻai keleawe a i ʻole kālā no nā ʻāpana Mo e hana ana ma lalo o 400 ℃;No nā mea uila a me nā ʻāpana hana ʻole e hana ana ma 400 ~ 650 ℃, Cu Ag, Au Ni, PD Ni a i ʻole Cu Ni nā mea kūʻai aku hiki ke hoʻohana ʻia;Hiki ke hoʻohana ʻia nā metala hoʻopiha metala maʻemaʻe me nā wahi hoʻoheheʻe kiʻekiʻe no nā ʻāpana e hana ana i nā wela kiʻekiʻe.Pono e hoʻomaopopo ʻia ʻaʻole ʻōlelo ʻia nā metala hoʻopihapiha hoʻopihapiha hoʻokumu i ka manganese, cobalt a me nickel e pale aku i ka hoʻokumu ʻana o nā pūhui intermetallic brittle i loko o nā hui brazing.

Ke hoʻohana ʻia nā ʻāpana TA a i ʻole Nb ma lalo o 1000 ℃, hiki ke koho ʻia nā ʻāpana keleawe, ka manganese, ka cobalt, ka titanium, ka nickel, ke gula a me ka palladium, me Cu Au, Au Ni, PD Ni a me Pt ​​Au_ Ni a Cu Sn solders i maikai wettability i TA a me Nb, maikaʻi brazing seam hana a me kiʻekiʻe hui pū ikaika.Ma muli o ka hana ʻana o nā metala hoʻopiha kālā i mea palupalu, pono e pale ʻia e like me ka hiki.No nā ʻāpana i hoʻohana ʻia ma waena o 1000 ℃ a me 1300 ℃, e koho ʻia nā metala maʻemaʻe Ti, V, Zr a i ʻole nā ​​mea hoʻoheheʻe e pili ana i kēia mau metala i hana i ka paʻa paʻa ʻole a me ka wai me lākou e koho ʻia e like me nā metala hoʻopiha piha.Ke kiʻekiʻe ka mahana o ka lawelawe, hiki ke koho ʻia ka metala hoʻopiha i loaʻa iā HF.

W. E nana i ka papa 13 no na metala hoopiha palapa no Mo, Ta a me Nb ma ka wela kiekie.

Papa 13 nā metala hoʻopihapiha hoʻopihapiha no ka hoʻopaʻa wela wela o nā metala refractory

2. ʻenehana brazing

Ma mua o ka brazing, pono e wehe pono i ka oxide ma ka ʻili o ka metala refractory.Hiki ke hoʻohana ʻia ka mīkini wili ʻana, ka puhi ʻana i ke one, ka hoʻomaʻemaʻe ultrasonic a i ʻole ka hoʻomaʻemaʻe kemika.E hana ʻia ʻo Brazing ma hope koke o ka hoʻomaʻemaʻe ʻana.

Ma muli o ka brittleness inherent o W, e mālama pono ʻia nā ʻāpana w i ka hana hui ʻāpana e pale aku i ka haki.I mea e pale aku ai i ka hoʻokumu ʻana o ka brittle tungsten carbide, pono e pale ʻia ka pilina pololei ma waena o W a me graphite.E hoʻopau ʻia ka pretressing ma muli o ka hana hoʻoheheʻe mua ʻana a i ʻole ke kuʻi ʻana ma mua o ka wili ʻana.He maʻalahi loa ka W i ka oxidize ke piʻi ka mahana.E lawa ke kiʻekiʻe o ke degere vacuum i ka wā o ka brazing.Ke hoʻokō ʻia ka brazing i loko o ka pae wela o 1000 ~ 1400 ℃, ʻaʻole e emi ka degere ʻana ma mua o 8 × 10-3Pa. I mea e hoʻomaikaʻi ai i ka mahana remelting a me ka mahana lawelawe o ka hui, hiki ke hoʻohui ʻia ke kaʻina hana brazing me. ka lāʻau diffusion ma hope o ka wili.No ka laʻana, hoʻohana ʻia ka solder b-ni68cr20si10fel e braze W ma 1180 ℃.Ma hope o ʻekolu hoʻomaʻamaʻa diffusion o 1070 ℃ / 4h, 1200 ℃ / 3.5h a me 1300 ℃ / 2h ma hope o ke kuʻi ʻana, hiki ke piʻi ka mahana lawelawe o ka hui brazed ma mua o 2200 ℃.

Pono e noʻonoʻo ʻia ka helu liʻiliʻi o ka hoʻonui ʻana i ka wela i ka wā e hui ai i ka hui brazed o Mo, a ʻo ka ʻāpana hui i loko o ka laulā o 0.05 ~ 0.13MM.Inā hoʻohana ʻia kahi mea paʻa, koho i kahi mea me kahi koena liʻiliʻi o ka hoʻonui wela.Hana ʻia ka mo recrystallization i ka wā e hoʻomāmā ai ka lapalapa ahi, ka umu ahi hoʻomalu, ka umu hoʻoheheʻe, ka umu hoʻokomo a me ka hoʻomehana kūpaʻa ma mua o ka mahana recrystallization a i ʻole ka emi ʻana o ka mahana recrystallization ma muli o ka diffusion o nā mea solder.No laila, i ka wā e kokoke ana ka mahana brazing i ka mahana recrystallization, ʻoi aku ka pōkole o ka manawa brazing, ʻoi aku ka maikaʻi.I ka wā e hoʻopaʻa ai ma luna o ka mahana recrystallization o Mo, pono e hoʻomalu ʻia ka manawa brazing a me ka helu hoʻoluʻu e pale aku i ka haki ʻana ma muli o ka hoʻoilo wikiwiki loa.Ke hoʻohana ʻia ka oxyacetylene flame brazing, kūpono ke hoʻohana ʻana i ka flux hui ʻia, ʻo ia hoʻi, ka borate ʻoihana a i ʻole ke kala brazing flux me ka flux wela kiʻekiʻe i loaʻa ka calcium fluoride, hiki ke loaʻa ka pale maikaʻi.ʻO ke ʻano o ka hoʻokomo mua ʻana i kahi ʻāpana o ke kahe keleawe kala ma ka ʻili o Mo, a laila e hoʻokomo i ka flux wela kiʻekiʻe.Loaʻa ka hana o ka flux brazing kālā ma kahi haʻahaʻa haʻahaʻa haʻahaʻa, a hiki i ka mahana ikaika o ka flux wela kiʻekiʻe ke hiki i 1427 ℃.

ʻOi aku ka maikaʻi o ka hoʻopaʻa ʻia ʻana o nā ʻāpana TA a i ʻole Nb ma lalo o ka ʻūhā, a ʻaʻole i emi ka degere ma mua o 1.33 × 10-2Pa.Inā hoʻokō ʻia ka brazing ma lalo o ka pale o ke kinoea inert, pono e hoʻoneʻe ʻia nā kinoea e like me carbon monoxide, ammonia, nitrogen a me carbon dioxide.Ke hoʻokō ʻia ka brazing a i ʻole ka brazing pale i ka lewa, e hoʻohana ʻia ka metala hoʻopihapiha hoʻopihapiha kūikawā a me ka flux kūpono.I mea e pale aku ai i ka TA a i ʻole Nb mai ka hoʻopili ʻana me ka oxygen i ka wela kiʻekiʻe, hiki ke hoʻopaʻa ʻia kahi papa keleawe a i ʻole nickel ma ka ʻili a hiki ke hoʻokō ʻia ka hoʻomaʻamaʻa diffusion annealing.